Production Machining

MAY 2018

Production Machining - Your access to the precision machining industrial buyer.

Issue link:

Contents of this Issue


Page 53 of 63

cleaning agents. Solvent cleaning is sometimes preferred, on the grounds that aqueous processes leave a part "too clean." This is because while cleaning is an essential part of surface preparation, the soil, notably the metalworking fluid, acts as a non-conductive coating. The more effective the soil removal, the higher the potential for corrosion. It is becoming more difficult to clean a product, in part because metalworking fluids have evolved and leave more residue. Manufacturers used to use "vanishing oils." ese oils left some residue on the part that protected the product from corrosion. e downside was that the oils vanished into the air, resulting in pollution. Given environ- mental mandates, metalworking fluids were reformulated to be less evaporative, which means they leave more complex residue on the part. is residue can interfere with subsequent assembly, coating and finishing opera- tions and must be removed using aggressive cleaning, resulting in a surface that is susceptible to corrosion. One solution is to clean and then forestall corrosion using a corrosion inhibitor to reduce conduction. However, any corrosion inhibitor is adding a contaminant to the surface. e right corrosion inhibitor depends on the customer. In an era of increased cleaning costs and diverse customer requirements, those who fabricate, stamp or machine metal parts may, out of necessity, avoid making a decision about the correct cleaning process or the optimal corrosion inhibitor. e machinist may not do any cleaning and/or may supply the product packed in oil. In this case, cleaning processes may require higher temperatures, stronger physical forces and longer cleaning and rinsing times than normal. More aggressive cleaning can lead to corrosion susceptibility. For complex supply chains, the customizing corrosion protection for a range of customers may require finesse. However, where there is a captive or dedicated machine shop, there is a simple, radical solution: communicate and coordinate! CONTRIBUTOR Barbara Kanegsberg and Ed Kanegsberg Ph.D., consultants with BFK Solutions, specialize in critical/precision and industrial product cleaning. For questions or to receive their newsletter, call 310-349-3614 or email info@ By Barbara Kanegsberg and Ed Kanegsberg Ph.D. Post-Cleaning Corrosion Prevention I n an industry where competition among machine shops can be fierce, it's critical to produce parts that are high quality and will stay that way for as long as possible. However, there are some obstacles that stand in the way of longevity and corrosion is one of them. Corrosion is the process by which metal surfaces are modified to form an oxidation product such as rust. To understand how corrosion works, consider the Corrosion Square. e parts of the corrosion square (Fig. 1) consist of an anodic area that supplies electrons, a cathodic area that consumes electrons, a conducting path between the two and oxygen or an oxidizing chemical. To forestall corrosion, remove at least one component of the square (Fig. 2). Surface prepara- tion, notably critical cleaning, must be understood and managed properly. Otherwise, the corro- sion square slips back together and corrosion happens. One key to success is understanding that cleaning, passivation and corrosion protection are separate activities with distinct functions. Cleaning is removing soil or unwanted matter, without damaging the surface. Passivation, typically surface treatment with an acid, is a modification that leaves the surface less susceptible to corrosion. e notion that passivation can replace cleaning is not true. If the soils are polar, such as salts, then passivation may be enough. However, if metalworking fluids are used, usually non-polar, organic compounds are present. Acid treatment won't remove most surface soils that accumulate during metal forming or fabrication. In fact, cleaning with water alone and then passivating is an invitation to corrosion. If the surface is not clean enough, passivation will not be consis- tent. ere will likely be poor coating adhesion, leading to rejoining of the conductive portion to the corrosion square. To effectively remove most soils, aqueous cleaning processes use basic (high pH) or sometimes near-neutral ANODE CATHODE OXIDIZER CONDUCTOR ANODE CATHODE OXIDIZER CONDUCTOR Fig. 1. The corrosion square. Fig. 2. The corrosion square with one corner removed. COMING CLEAN 52 PRODUCTION MACHINING :: MAY 2018

Articles in this issue

Links on this page

Archives of this issue

view archives of Production Machining - MAY 2018