CRAFTSMAN'S CRIBSHEET Distortion in Heat Treatment Technical Regulatory Management Quality Tere are two kinds of distortion that can result from a heat-treating process in steel: dimensional distortion and shape distortion. Dimensional Distortion can take place upon heating when steel parts change volume as they change crystal structure. When heated parts are quenched, their internal crystal structure changes again. When the quenched parts are tempered, the resulting volume change may not be sufcient to ofset the changes from the prior heating and transformations. Tis change of volume can cause dimensional distortion. Te rule of thumb that I have used for medium carbon alloy steels is to expect a change in linear dimensions of about 0.125 percent maximum. Tat is, one eighth of a percent of the linear dimensions could be the change encountered from heat treatment and quench. It generally is less, but 0.125 percent gives me a rule of thumb to evaluate capability to hold dimensions after heat treat. Shape Distortion (warpage) as a result of heat treatment is a result of processing or design issues rather than the expected phase changes of the material. Eight reasons steel parts can warp upon quench and tempering: 1. 2. 3. 4. 5. 6. 7. 8. Rapid heating Overheating Non-uniform heating Non-uniform cooling Non-uniform agitation Water contamination in oil Large changes of mass and section Asymmetric features Rapid heating can cause stresses to develop in parts because of excessive temperature gradients. Overheating similarly lowers mechanical properties, potentially leading to parts sagging or creeping depending on orientation in the furnace. Non-uniform heating also creates diferences in properties within the parts as well as leading to incomplete transformation products or hybrid structures upon quenching. Non-uniform cooling allows unbalanced stresses to develop during the quench, as does non-uniform agitation of quench medium. Often, nonuniform heating or cooling result from the way parts are stacked or piled in the basket or on the belt such that gradients of temperature are created. Water contamination in oil is difcult to fgure out, but in addition to warped parts, inconsistent hardness readings between parts or on the same part are a sign of this. Parts with large section changes or that have asymmetric features are also more likely to warp than parts with balanced and uniformly distributed mass, regardless of process control. Choosing steels with higher hardenability (alloys rather than plain carbon steels) and fner grain size and paying attention to the details of loading, time at temperature and quenchant delivery are all steps that can minimize shape distortion, even when part design is less than optimum. Miles Free – Director of Industry Research and Technology productionmachining.com :: 19